30 J
Standard Duty Pipe Jacketing
Meets ASTM C1136, Type I, II, III, IV
FACING COMPOSITION |
DESCRIPTION |
VALUES (ENGLISH) |
VALUES (Metric) |
Kraft |
High Intensity White |
45 lbs /
3000 ft2 |
73 gm /
m2 |
Adhesive |
Flame Resistant |
|
|
Reinforcing |
Tri-directional
Fiberglass |
5 / inch (MD)
5 / inch (XD) |
20 / 100 mm (MD)
20 / 100 mm (XD) |
Barrier Coating |
Elastomeric Polymer |
0.0002 inch |
5.1 micron |
Foil |
Aluminum |
0.0003 inch |
7.6 micron |
PHYSICAL PROPERTIES |
TEST METHOD |
VALUES (ENGLISH) |
VALUES (Metric) |
Basis Weight |
Scale |
29 lbs / 1000 ft2 |
142 gm / m2 |
Permeance (WVTR) |
ASTM E96
Procedure A |
0.02 perm
(grains/hr.ft2.in Hg) |
1.15 ng / N.s |
Bursting Strength |
ASTM D774 |
65 psi |
4.6 kg / cm2 |
Puncture Resistance |
ASTM C1136 |
85
beach units |
2.5
Joules |
Tensile Strength |
ASTM C1136 |
55 lbs/inch width (MD)
50 lbs/inch width (XD) |
9.6 kn / m (MD)
8.8 kn / m (XD) |
Caliper / Thickness |
Micrometer |
0.009 inch |
229 micron |
Accelerated Aging |
30 Days @
95% RH, 120°F (49°C) |
No Corrosion
No Delamination |
No Corrosion
No Delamination |
Low Temperature Resistance |
ASTM D1790
-40°F (-40°C) |
Remains Flexible
No Delamination |
Remains Flexible
No Delamination |
High Temperature Resistance |
4 hours @
240°F (116°C) |
Remains Flexible
No Delamination |
Remains Flexible
No Delamination |
Water Immersion |
24 hours @ 73°F (23°C) |
No Delamination |
No Delamination |
Mold Resistance |
ASTM C665 /
C1338 |
No Growth |
No Growth |
Dimensional Stability |
ASTM D1204 |
0.25% |
0.25% |
Emissivity (White Kraft Side) |
ASTM E408 |
0.9 |
0.9 |
Emissivity (Foil Side) |
ASTM E408 |
0.03 |
0.03 |
Fire Testing |
ASTM E84 / UL 723 |
CAN ULC-S102M |
Film Side |
Kraft Side |
Film Side |
Kraft Side |
Flame Spread |
5 |
20 |
5 |
20 |
Smoke Developed |
0 |
10 |
0 |
10 |
Physical Properties based upon statistical averages, Weight / Thickness +/- 10%